Ab-initio studies on the phonons of BaTiO3 polytypes: pressure dependences with a hybrid functional

Original · EN

We report the first principles investigations on the phonons of three polytypes of BaTiO3 (BTO): paraelectric (PE) cubic Pm-3m and two ferroelectric (FE) phases, tetragonal P4mm and rhombohedral R3m. The phonon frequencies calculated using various exchange-correlation functionals, including density functional theory, Hartree-Fock approximation, and their hybrids were reviewed. The pressure-induced interplays between the modes form individual phases were explored by calculating the phonon modes as a function of pressure, P from -15 to 230 GPa. The pressure-sensitive modes of the FE phases showed softening and converged to the modes of the PE phase at pressures below 10 GPa. These results on the FE phases can be interpreted as phonon-precursors for a change in symmetry from low- to high-symmetry and partly as a theoretical explanation for the pressure-induced mode-coupling behaviors reported by Sood et al. [Phys. Rev. B 51, 8892 (1995)]. As pressure is applied further beyond 50 GPa to the cubic PE phase, the lowest F1u mode softens again and diverges into two separate modes of tetragonal FE P4mm at above 150 GPa. These phonon-branching behaviors at high pressures provide a clear re-confirmation of the re-entrant ferroelectricity predicted in [Phys. Rev. Lett. 95, 196804 (2005); Phys. Rev. B 74, 180101 (2006); ibid. 85, 054108 (2012)]. The high-pressure-re-entrant FE polarization was not found in the rhombohedral structure. Instead, the centosymmetric R-3m phase was favored at above 30 GPa. The phonon modes calculated for the phonon-propagation vectors in the high-symmetry directions show that the Pm-3m phase exhibits polar instability at the Γpoint and non-polar instability at the X, M, and R points under high pressure.