The high-pressure synthesis of MgB2
Prikhna, T. A. · Gawalek, W. · Surzhenko, A. B. · Sergienko, N. V. · Moshchil, V. E. · Habisreuther, T. · Melnikov, V. S. · Dub, S. N. · Nagorny, P. A. · Wendt, M. · Savchuk, Ya. M. · Litzkendorf, D. · Dellith, J. · Kracunovska, S. · Schmidt, Ch.
Original · EN
The high-pressure synthesis is one of the most promising methods to produce MgB2 superconductive (SC) material. The available high-pressure apparatuses have working volume up to 100 cm3 which allows samples up to 60 mm in diameter to be manufactured. By a short-term (1h) high-pressure (2GPa) synthesis from Mg and B we have obtained samples 2.4-2.5 g/cm3 in density, 12.1-15.6 GPa in microhardness (under 4.96 N load), 170-200 kA/cm2 at 10 K and 58-62 kA/cm2 at 20 K in critical current density at a magnetic field of 1T. Samples demonstrated 8.5 T irreversible field at 10 K and 5.5 T at 20 K. The Ta positive influence on SC properties of MgB2 has been observed.
English translation
This paper has no Arabic translation yet. Be the first: it takes a few seconds, and the result is stored for every future reader.